1. … should not be deposited. A Buffer layer with OA 4370, OA MnCr or ER 100 is recommended.  … 67-69 HRc hardfacing alloy, for fire gratings, …
  2. … construction of boilers and pipes (15Mo3).Hydrogen content (HD < 5 ml/100 g). … Typ 0,5Mo   ISO 15608: ≤ 460 MPa ; 1.1, 1.2,(~1.3) 1.5415, …
  3. … are required at sub zero temperatures. Hydrogen content HD < 4 ml/100 g. … Reh < 790 MPa  S620Q, S620QL, S690Q, S690QL, S620QL1-S690QL1,  L480 - L550, X65, X80, X90, X100 XABO 90, Domex 700 MC   … E 12018-G … A 5.5: E 12018-G … 18275-A: E …
  4. … low spatter loss, easy slag removal and hydrogen content below 3 ml/100gr. even after long unconditioned storage. … CuNi, Reh ≤ 460MPa ISo …
  5. … excelent mechanical properties at low temperatures.HD < 5 ml/100 … Reh ≤ 460 MPa ISO 15608: 1.2, 1.3, 2.1, 9.2  1.5637, 1.6217, …
  6. … offers superior wear protection, retaining its hardness up to 600ºC (1000ºF) with significant resistance to oxidation. … Aircraft gas …
  7. … structural steels with Rp0,2 > 500 MPa. Low hydrogen content HD < 3 ml/100g even after long storage. … Reh ≤ 500 MPa, ISO 15608: 1.3, 2.1, 2.3 …
  8. Brand: ITW Elga - Hobart
    CEWELD Product: AA R500, AA R500SR
    … are seamless and therfore they offer a lower hyrogen content (≈2 ml/100gr) even after many years of storage. Due to less preheating …
  9. … very good weldability, suitable for high operating temperatures up to 1100°C. … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21,  23% Cr, 12%Ni Type 1.2780, 1.4541, 1.4550, 1.4710, …
  10. … welding properties and extreme low hydrogen content below HD 3 ml/100gr weld metal. The weldmetal is suitable for longer post weld heat …