… at 600-800 °C. The interpass temperature should not exceed 300 °C. … 1.4340, 1.4710, 1.4745, 1.4746, 1.4712, 1.4762, 1.4713, … 27 4, AISI 327, 442, 446, ASTM A 297 HC UNS S44200, 44600, J92605, J93005, J92605  … 4820 AC … 3581-A: E 25 4 R 32 …

… concentrated (98.5 %) sulphuric acid at temperatures of up to 150 °C (300 °F). … CEWELD® SA Nicro 690 Strip is mainly used for ESW and SAW …

… used without further treatment. Coating thickness should not exceed 300 μm. Maximum operating temperature is 540°C (1004°F). Powder type: …

… of up to 450ºC. The recommended preheat temperature is 200ºC - 300°C unless the base material requires a higher preheat temperature. …

Type C Mn Si Cr Ni Mo Nb N W Other PREn 307 Si <0.12 6.5 0.8 18.5 8.5           19 308 LSi <0.03 1.7 0.8 21.0 10.0 <0.75         19 308 H <0.03 1.7 0.8                 309 LSi 0.05 1.8 0.45 21.0 10.0 <0.5           309 H <0.12 1.8 0.5 24.0 13.0             310 0.10 1.8 0.5 26.0 21.0 <0.3           …

… the weld metal. The preheat and interpass temperature should be 200 – 300ºC. A tempering 730 – 800ºC is possible. … 1.4000, 1.4002, 1.4016, … X2CrTi17, X10CrSi6, X10CrAlSi7, X10CrAlSi13, X10CrAlSi18 UNS S40300, S40500, S40900, S41000, S42900, S43000, S43035, S43036, S43100, S44200  AISI 403, 405, 409, 410, 429, …

… hardness of the fused tungsten carbides (WSC) of approx. 2300 HV imply the high build-up wear resistance. It is a dip-coated …

… and interpass temperature 400-450 °C (austenitic welding) or 250-300 °C (martensitic welding). Root passes should principally be welded …

… tips and by grinding. The hardness of the deposit will degrease 16% at 300°C and about 30% at 600°C. Excellent alloy against thermal shock, …

… of. In case of sensitive base material preheating is recommended at 300-400°C. … 600 HB, T Fe 8 … MA 600 (1.4718) … A 5.21: ERFeCr-A … …