SMAW beklede elektroden

Dur CE-Tube WC2

Due to the complex carbide combination of Cobalt, Chromium, Aluminium, Zirconium and a extreme high Tungsten content the wear resistance against abrasion is 4 till 8 times better in comparison with C-Cr. alloys.
Hard facing knowledge is based on practical experience and years of testing many different procedures and alloys. For your typical application we recommend to consult us for a tailor made welding procedure in order to achieve the best possible results for each job.
1) up to 3 times faster ! (less current with more deposit)

7016

Double-coated semi basic CTOD tested electrode with excellent welding properties in difficult positions and high mechanical properties. It is particularly suited for poor welding machines with low open voltage on AC and DC+. Excellently suited for old and rusty material because of its stable and intensive arc. Well suited for root runs and in the maintenance and repair sector due to its absolute insensitiveness for rust or diluted base metals.
Hydrogen content: <10ml/100gr weld metal.

4430 Ti

The weld deposit is scale-resistant up to approx. 800°C in normal atmosphere and oxidizing gases. Extreme stable arc on both AC and DC+ with no spatter losses. The weld deposit is capable of taking a high polish.

12018-Mo

Basic electrode with excellent welding characteristics, recommended for welding fine grained similar alloyed high yield strength steel (> 960 Mpa) in case high impact values are required at sub zero temperatures. Hydrogen content (HD < 4 ml/100 g).

10018-D2

Basic electrode with excellent welding characteristics,  Hydrogen content (HD < 3 ml/100 g). Meets NACE requirements MR0175/ISO15156-2.

4316 Kb

The weld deposit is scale-resistant up to approx. 800°C in normal atmosphere and oxidizing gases. The weld deposit is capable of taking a high polish.

E NiCro 625 HLS

Latest generation high recovery type (170%) guarantees optimum deposit rate and metallurgical quality and attractive welder appeal in the PA-PB position.
Very good resistance against pitting corrosion and crevice corrosion.
Very good against acid, neutral or alkaline media, with or without chlorides.
Very good resistance at high temperatures, especially against oxidation.
 

Dur E 64

Due to the high Mo-content, abrasion resistance can be kept up to working temperatures of 600ºC ; the hardness is still 40-45 HRc at these temperatures. For hardfacing of more than 3 layers it is necessary to buffer with an electrode like DUR E 350 Kb that delivers a welding deposit of less hardness. Overlays on steel with high tensile strength have to be buffered with Croni 29/9 HL or 4370 HL.

Equivalent in FCAW: OA 64

E AlSi 12

Very good weldability with good penetration and porosity free deposit, Unique self lifting slag and improved coating against moisture pick up.
 