1. … may be used in applications at sustained elevated temperatures. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … G-AlSi10Mg, G-AlSi11, G-AlSi12 (Cu), …
  2. … 15CrMoV6 provides  high  strength, actual strength being dependent on heat treatment  Preheat,  interpass  temperature and PWHT will  be dependent  on …
  3. … of up to 450°C and offers scaling resistance up to 950°C. Preheating at 250 °C and stress relieving at 800 °C is recommended if this … the base material, the higher the hardness of the weld metal. The preheat and interpass temperature should be 200 – 300ºC. A tempering 730 – …
  4. … the pure aluminium grades. Heavy parts and thicker plates should be preheated (150°C), prior to welding. At the same time, it keeps the … and workability. It can be strengthened by cold working, but not by heat treatment. … Al99,0 Al.99,5 Al.99,7 E-Al., 99,5, 3.0205, 3.0255, …
  5. … CEWELD® 410 Tig is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% … Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding. … 1.4000, 1.4001, 1.4002, 1.4003, 1.4006, …
  6. … CEWELD 410 is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% … Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding. … 1.4000, 1.4001, 1.4002, 1.4003, 1.4006, …
  7. … For welding heat-resistant austenitic steels of the 25% Cr, 20% Ni types. CEWELD … oxidation depend on cycle frequency. In general the alloy is heat resistant up to 1200 °C. This alloy can withstand relatively …
  8. … spatter free welding with very low current. Due to the very low heat input and unique composition of Ni the transition zone will stay … case off multi-layer welding. The weld metal will show no undercut !Preheating is normally done to slow down the cooling speed, in case you …
  9. … bright, almost smut-free welds. Not recommended for anodizing. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … AlMgSi 0, AlSiMg (A), AlSi 1 MgMn, …
  10. … may be used in applications at sustained elevated temperatures. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … G-AlSi10Mg, G-AlSi11 G-AlSi12 (Cu), …