1. … product or company presentations and can accommodate up to 100 people. The layout of the room can be adapted to your needs, for …
  2. … construction of boilers and pipes (15Mo3).Hydrogen content (HD < 5 ml/100 g). … Typ 0,5Mo   ISO 15608: ≤ 460 MPa ; 1.1, 1.2,(~1.3) 1.5415, …
  3. … should not be deposited. A Buffer layer with OA 4370, OA MnCr or ER 100 is recommended.  … 67-69 HRc hardfacing alloy, for fire gratings, …
  4. … are required at sub zero temperatures. Hydrogen content HD < 4 ml/100 g. … Reh < 790 MPa  S620Q, S620QL, S690Q, S690QL, S620QL1-S690QL1,  L480 - L550, X65, X80, X90, X100 XABO 90, Domex 700 MC   … E 12018-G … A 5.5: E 12018-G … 18275-A: E …
  5. … low spatter loss, easy slag removal and hydrogen content below 3 ml/100gr. even after long unconditioned storage. … CuNi, Reh ≤ 460MPa ISo …
  6. … fluxcored wires are the lowest on the market today (between 2 and 3 ml/100gr weld metal). The demands for welding consumables are getting …
  7. … to high temperatures (most suitable temperature range is 850 - 1100 °C), high creep strength, very good resistance to isothermal and, …
  8. … excelent mechanical properties at low temperatures.HD < 5 ml/100 … Reh ≤ 460 MPa ISO 15608: 1.2, 1.3, 2.1, 9.2  1.5637, 1.6217, …
  9. … structural steels with Rp0,2 > 500 MPa. Low hydrogen content HD < 3 ml/100g even after long storage. … Reh ≤ 500 MPa, ISO 15608: 1.3, 2.1, 2.3 …
  10. … humidity before the general requirement of less than 5ml hydrogen in 100gr weld metal is exceeded. The most important steps to prevent …