… welding properties. Stainless deposit with low carbon content. Low heat input is recommended to avoid pronounced grain coarsening. Absence …

… of braking out or chipping of. In case of sensitive base material preheating is recommended at 300-400°C. … 600 HB, T Fe 8 … MA 600 (1.4718) …

… hardness of 49-53 HRc at room temperature. The weld deposit is high heat resistant up to 900°C. Dur 12 offers a low coefficient of friction …

… micro-structure For the best results, welding must be done in a low heat input procedure and is not recommended for multi-pass applications …

… 16% at 300 °C and about 30% at 600 °C. The weld deposit is high heat resistant up to 900 °C.  … Steam-valves, High temperature liquid …

… of braking out or chipping of. In case of sensitive base material preheating is recommended at 300 - 400 °C. Old Hardfacing layers should be …

… deposit is capable of taking a high polish.Structure: Austenite with delta ferrite UNS 34780 … ISO 15608: 8.1 / TüV Groupe 29 (+22+21) / …

… cleaning required with very low spatter loss. Weld metal is heat treatable.  … Reh ≤ 890 MPa ISo 15608: 5.1 1.7220, 1.7225, 1.7228, …

… 3 ml/100gr weld metal. The weldmetal is suitable for longer post weld heat treatments as applied in Riser applications. … Reh ≤ 550 MPa, ISo …

… steels. It can also be used for constructions that needs post weld heat treatment after welding and still offers excellent impact …