- … up to working temperatures of 600 ºC ; the hardness is still 40-45 HRc at these temperatures. For Hardfacing of more than 3 layers it is …
- … for all other spraying alloys. Hardness, coating macro: approximately HRc 22. Maximum working temperature: approximately 850 °C … Shafts, …
- … normal cutting tools, grinding is possible. Hardness approximately 45 HRc. The deposit can be tempered. … 1.4016, 1.4511 X6Cr17, X3CrNb17 …
- … deposit will degreas 20% at 600°C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high heat resistant up to … due to its resistance to metal-to-metal wear. … 46-48 HRc, Stellite 12 alloy with high temperature and abrasion resistance, …
- … and metallurgically bonded to substrates due to diffusion. ▪ hardness: HRC 22-25 ▪ applicable up to approx. 820 °C … . … Powder Nickel 3 …
- … normal cutting tools, grinding is possible. Hardness approximately 50 HRc … Flame spray, electric spray and high speed flame spray. … SP …
- … deposit will degrees 20% at 600°C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high heat resistant up to …
- … deposit will degrees 20% at 600 °C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high heat resistant up to … due to its resistance to metal-to-metal wear. … 46-48 HRc, Stellite 12 Alloy with high temperature and abrasion resistance, …
- … Due to the low dilution with the base metal a hardness exceeding 50 HRc can be achieved already in the first layer. Multiple layers can be … full hardness at the final layer. Flux to be used FL 830 ESH … 52-58 HRc electro slag and / or submerged arc strip for hardfacing against …
- … to metal wear in hot working circumstances. The hardness is 45-53 HRc. Best properties are achieved with our agglomerates flux FL 838 or …