6013 T

type 
Thick coated rutile electrode for SMAW welding
applications 
Yacht building, wagon building, train, ship building, vessel, general constructions
Properties 

6013 T is a thick coated electrode for joining and surfacing steel structures of all kinds in mechanical engineering, body and wagon building, in the fabrication of vessels and containers, and in shipbuilding. The 6013 T is eminently weldable and possesses excellent welding properties in all positions except vertically down. Easy strike, no spatter losses. Very easy slag removal. Smooth, finely rippled seam surface and low fume.

classification
AWS 
A 5.1: E 6013
EN ISO 
2560-A: E 42 0 RR 12
DIN 
1913: E 51 22 RR 6
Suitable for 
DIN:
Unalloyed steels:
Boiler plates:
Pipe steels:
-
Shipbilding plates:
Steel castings:
Thin sheets:

-
St 33 to St 52.3
HI, HII, 17 Mn4
St 35 to St 52.4
StE 210.7 to StE 360.7
A, B, D
GS-38 to GS-52
1623/1

W.Nr.:
1.0035 to 1.0570
1.0345, 1.0425, 1.0481
1.0308 to 1.0581
1.0307 to 1.0582
1.0440, 1.0472, 1.0475
1.0416 to 1.0551

 

approvals 
TUV, CE approved
welding positions: 
weld metal weight %

C

Mn

Si

Cr

Ni

Mo

0.08

0,6

0.45

-

-

-

mechanical properties

Heat

RP0,2

Rm

A5

Impact Energy (J) ISO-V

Hardness

Treatment

(N/mm2)

(N/mm2)

(%)

0°C

-40°C

-60°C

HRc / HV

AW

>360

510-610

>22

>47

AW: as welded
redrying temperature 
140°C / 2hr
welding parameters packing

Welding Parameters

Packing

D (mm)

Length (mm)

Current (A)

kg / can

kg / 6pack

kg / 1000

2,0

300

50-70

2.2

13.2

11.1

2,5

300

65-90

2.6

15.6

20.46

3,2

350

100-140

2.6

15.6

34.78

4,0

450

140-180

3.2

19,2

72

5,0

450

190-240

3.1

18.6

105.9

6,0

450

240-290

3.0

18

150

Disclaimer: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained, the information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and any liability incurred from any reliance thereon is expressively disclaimed. Typical data are those obtained when welded and tested in accordance to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Other tests and procedures may produce different results. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application. The selection and use of specific products is solely within the control of, and remains the sole responsibility of the customer. The right to change design and/or specifications without notice is reserved.