1. … feather. The deposit is not mashinable or forgeable. Only grinding with diamond tools is possible.Dur R (Ni) is available as a 500 mm … cast iron or Mn-steel. The main applications are hardfacing and rebuilding of stabilisers and other oilfield tools where maximum protection …
  2. … Excellent welding properties with high buildup capacity and low dilution rate when … medias. Excellent fatigue strength and creep properties. … Cladding against high temperature, radiant heater tubes, furnace rolls, …
  3. … Coating microhardness: 800-1300 HV0.3 Sales units: Particle size* (DIN EN 1274 3.3): -45+22 μm (*other sizes on request) -38+15 μm -25+10 …
  4. … wetting. Due to the excellent wetting and low melting point welding speeds can be achieved upto 2 mtr/min. The weld deposit offers a …
  5. … SP NiAl is recommended. The spray deposit is only machinable by grinding. … Cement industry, pumps, mixer blades, sleeves, mixers, shear …
  6. … deposits are air-hardenable that can normally be heat-treated after welding. … 1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008,  1.4021, … X15Cr13, X20Cr13, G-X10Cr13 AISI 410, 420 … 410 Tig … A 5.9: ER410 … 14700: S Fe7 … 14343-A: W Z 13 …
  7. … bead appearance without slag residues. Best to be used with welding flux FL 915 … 1.4317, 1.4313, 1.4407, 1.4414,    GX4CrNi13-4, … GX4CrNiMo13-4  ACI Gr. CA 6 NM … SACW 410 NiMo … A 5.9: EC410NiMo … 14700: T Fe7 …
  8. … metal has low levels of tramp elements (eg. Sn, As, Sb and P) providing a low Bruscato Factor.(X …
  9. … industry such as riser pipes that often are heat treated after weding.. … P460NL1, P460ML1, S460Q-S550Q, S460QL-S550QL, P460Q-P500Q, …
  10. … Dur 6 Mo is free of Ni, Be. and Cadmium according EN ISO 22674. The alloy offers extreme low friction properties … against scalling, abrasion and extreme pressure loads. … Overlay welding on wear parts. 3D printing of parts for medical applications according class IIa medical device in accordance with annex IX rule 8 of the …