… practical welding tests and process qualification tests. After welding cooling to 90±10 °C, followed by tempering at 760 °C for three minutes …

… strength should be buffered with CroNi 29/9 HL or 4370 HL. Up to 3 times faster! (less current with more deposit) No slag losses compare …

… the latest technologie. Due to the manufacturing process and two times anealing during the drawing process at 580ºC the hydrogen content …

… with very low hydrogen content. Suitable for heat treatment. Step cooling is possible. High reserve of toughness and crack resistance. … …

… resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, E Dur 12 can be used to protect …

… resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, Dur 12 can be used to protect …

… resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, Dur 12 can be used to protect …

… Welding instructions: - Preheating for sections >6 mm from 150 till 300 ºC is recommended. Use the normal standard welding techniques. …

… constructions that needs post weld heat treatment after welding and still offers mechanical properties confirming 5Y46 class. Due to the …

… against heavy abrasion. Usualy the maximum number of layers is 2 till 3 but when using a special stringer build up technick with release …